310s不锈钢管与309s不锈钢的耐高温性能介绍

时间:2018-08-03 浏览:
309s不锈钢板310s不锈钢板归于耐热型奥氏体不锈钢,成分特点为高Cr高Ni。309S和310S为两商标的低碳版别。在氧化性介质中,两型不锈钢都兼具优秀耐蚀功能和优秀高温力学功能。
 
GB/T 20878 ASTM A276 JIS G4303 EN 10088-1
16Cr23Ni13
(2Cr23Ni13)
309 X12CrNi23-13
1.4833
06Cr23Ni13
(0Cr23Ni13)
309S SUS 309S
20Cr25Ni20
(2Cr25Ni20)
310 X15CrNiSi25-21
1.4841
06Cr25Ni20
(0Cr25Ni20)
310S SUS 310S X8CrNi25-21
1.4845

310s不锈钢管厂家

耐高温不锈钢板国标GB和日标JIS的成分均与美标ASTM共同,欧洲标准的规定则略有不同。
 
GB 16Cr23Ni13
(2Cr23Ni13)
06Cr23Ni13
(0Cr23Ni13)
20Cr25Ni20
(2Cr25Ni20)
06Cr25Ni20
(0Cr25Ni20)
ASTM 309 309S 310 310S
JIS SUS 309S SUS 310S
C ≤0.20 ≤0.08 ≤0.25 ≤0.08
Si ≤1.00 ≤1.00 ≤1.50 ≤1.50
Mn ≤2.00 ≤2.00 ≤2.00 ≤2.00
P GB:≤0.040
ASTM:≤0.045
≤0.045 GB:≤0.040
ASTM:≤0.045
≤0.045
S ≤0.030 ≤0.030 ≤0.030 ≤0.030
Cr 22.00~24.00 22.00~24.00 24.00~26.00 24.00~26.00
Ni 12.00~15.00 12.00~15.00 19.00~22.00 19.00~22.00

 
310s不锈钢管厂家

商标 X12CrNi23-13
1.4833
X15CrNiSi25-21
1.4841
X8CrNi25-21
1.4845
C ≤0.15 ≤0.20 ≤0.10
Si ≤1.00 1.50~2.50 ≤1.50
Mn ≤2.00 ≤2.00 ≤2.00
P ≤0.045 ≤0.045 ≤0.045
S ≤0.015 ≤0.015 ≤0.015
Cr 22.00~24.00 24.00~26.00 24.00~26.00
Ni 12.00~14.00 19.00~22.00 19.00~22.00
N ≤0.11 ≤0.11 ≤0.11
 
商标 16Cr23Ni13
(2Cr23Ni13)
06Cr23Ni13
(0Cr23Ni13)
20Cr25Ni20
(2Cr25Ni20)
06Cr25Ni20
(0Cr25Ni20)
密度(g/cm3)20℃ 7.98 7.98 7.98 7.98
熔点(℃) 1398~1453 1397~1453 1398~1453 1397~1453
比热容
[kJ/(kg·K)]0~100℃
0.50 0.50 0.50 0.50
热导率
[W/(m·K)]
100℃ 13.8 15.5 14.2 16.3
500℃ 18.7 18.6 18.6 21.5
线膨胀系数
(10-6/K)
0~100℃ 14.9 14.9 15.8 14.4
0~500℃ 18.0 18.0 17.5 17.5
电阻率
(Ω·mm2/m)20℃
0.78 0.78 0.78 0.78
纵向弹性模量
(kN/mm2)20℃
200 193 200 200
磁性 冷变形后稍有磁性
(数据来历:GB/T 20878-2007)
 
在淡薄、氮化或碳化的空气条件中,309(309S不锈钢管)和310(310S不锈钢管)两种不锈钢的体现不如600合金(UNS N06600)或800合金(UNS N08800),但与大多数耐高温合金比较,两者具有更好的抗高温腐蚀性。
 
因为高温功能和耐蚀功能的杰出合作,两型不锈钢广泛应用于高温防腐蚀设备中,例如锅炉、压力容器、冶金和石油化工等行业之设备零部件。

 
309 接受980℃以下重复加热的抗氧化钢。
加热炉部件,重油燃烧器。
309S 比304耐氧化性好,可接受980℃以下
重复加热。炉用资料。
310 接受1035℃以下重复加热的抗氧化钢,
炉用部件、喷嘴、燃烧室。
310S 比309S抗氧化性好,可接受1035℃
加热。炉用资料,轿车净化装置用资料。